NFCByte

Outdoor

4 materials available

UV resistance, weathering, outdoor use

ASA

100°CHigh

Like ABS but with excellent UV resistance. Does not yellow, perfect for outdoor use.

Max Temp

100°C

Strength

High

Chemical

Medium

Flexibility

Rigid

UV resistantOutdoorDoes not yellowDurable

PC-PBT

PC/PBT Blend

107°CHigh

PC/PBT blend with excellent low-temperature toughness (-30°C) where other plastics become brittle. Acid resistant. Ideal for automotive exterior: bumpers, roof rails, handles.

Max Temp

107°C

Strength

High

Chemical

High

Flexibility

Rigid

Tough at -30°CAutomotive exteriorAcid resistantLow moisture absorption

Physical Properties

Density1.2 g/cm³

Melt Index16-22 g/10min

Melting temp223°C

Glass Transition140°C

Vicat139°C

HDT 1.8 MPa90.8°C

HDT 0.45 MPa107.4°C

Water absorption0.26%

Mechanical Properties

Young's Modulus (XY)1849 ± 103 MPa

Young's Modulus (Z)1659 ± 66 MPa

Tensile strength (XY)43.2 ± 0.5 MPa

Tensile strength (Z)28.6 ± 0.4 MPa

Elongation (XY)4.6 ± 0.7%

Elongation (Z)1.8 ± 0.3%

Impact strength (XY)21.4 ± 0.3 kJ/m² (15 @ -30°C)

Chemical Resistance

AcidsResistente

AlkaliParzialmente resistente

SolventsNon resistente

Oils & greaseN/A

Print Settings

Nozzle temp260-280°C

Bed temp100-115°C

Speed30-50 mm/s

Drying90°C, 2h (annealing)

Indicative values. Actual performance depends on print parameters.

PAHT-CF

Nylon-CF

194°CVery High

High-temp nylon with carbon fiber. Maintains excellent mechanical properties even in humid environments. For functional prototypes, fixtures, molds and low-volume production.

Max Temp

194°C

Strength

Very High

Chemical

High

Flexibility

Rigid

194°C HDTMoisture resistantMolds & fixtures92 MPa tensile

Physical Properties

Density1.06 g/cm³

Melt Index14.4 ± 2.0 g/10min

Melting temp225°C

Glass Transition70°C

Vicat220°C

HDT 1.8 MPa170°C

HDT 0.45 MPa194°C

Water absorption0.88%

Mechanical Properties

Young's Modulus (XY)3860 ± 230 MPa

Young's Modulus (Z)2180 ± 130 MPa

Tensile strength (XY)92 ± 7 MPa

Tensile strength (Z)47 ± 5 MPa

Elongation (XY)8.4 ± 1.8%

Elongation (Z)4.1 ± 1.2%

Impact strength (XY)57.5 ± 3.4 kJ/m² (22.8 notched)

Impact strength (Z)13.3 ± 0.8 kJ/m²

Chemical Resistance

AcidsNon resistente

AlkaliNon resistente

SolventsParzialmente resistente

Oils & greaseResistente

Print Settings

Nozzle temp260-290°C

Bed temp80-100°C

Speed<100 mm/s

Drying80°C, 8-12h

Indicative values. Actual performance depends on print parameters.

PA612-CF15

Nylon-CF

PA6+PA12 / Carbon Fiber 15%

175°CVery High

PA6+PA12 copolyamide with 15% carbon fiber. Lower moisture sensitivity than PA6/66, better mechanical properties than PA12. Warp-Free technology.

Max Temp

175°C

Strength

Very High

Chemical

Medium

Flexibility

Rigid

175°C HDTLow moisture sensitivity92 MPa tensileDimensionally stable

Physical Properties

Density1.03 g/cm³

Melt Index9.9 g/10min

Melting temp210°C

Vicat206.2°C

HDT 1.8 MPa114°C

HDT 0.45 MPa175°C

Water absorption2.2%

Mechanical Properties

Young's Modulus (XY)5137 ± 192 MPa

Young's Modulus (Z)2786 ± 78 MPa

Tensile strength (XY)91.9 ± 2.0 MPa

Tensile strength (Z)48.3 ± 3.9 MPa

Elongation (XY)2.6 ± 0.2%

Elongation (Z)2.1 ± 0.2%

Impact strength (XY)29.9 ± 1.6 kJ/m² (8.1 notched)

Impact strength (Z)12.6 ± 1.4 kJ/m²

Chemical Resistance

AcidsNon resistente

AlkaliParzialmente resistente

SolventsNon resistente

Oils & greaseResistente

Print Settings

Nozzle temp250-300°C

Bed temp40-50°C

Speed<300 mm/s

Drying100°C, 10h

Indicative values. Actual performance depends on print parameters.